1 ct. |
Lincoln - Memorial Reverse |
UNITED STATES |
|
|
- Diameter: 19,00 mm
- Thickness: 1,55 mm
- Weight: 2,50 gr
- 95% Cu, 5% Tin and Zn.
|
Cdb |
Year |
Mint |
Mintage |
Notes |
B017079 |
2008 |
Philadelphia |
2.569.600.000 |
|
1 ct. |
Lincoln - Memorial Reverse |
UNITED STATES |
|
|
- Diameter: 19,00 mm
- Thickness: 1,55 mm
- Weight: 2,50 gr
- 95% Cu, 5% Tin and Zn.
|
Cdb |
Year |
Mint |
Mintage |
Notes |
B017080 |
2008D |
Denver |
2.849.600.000 |
|
1 ct. |
Lincoln - Memorial Reverse |
UNITED STATES |
|
|
- Diameter: 19,00 mm
- Thickness: 1,55 mm
- Weight: 2,50 gr
- 95% Cu, 5% Tin and Zn.
|
Cdb |
Year |
Mint |
Mintage |
Notes |
B017081 |
2008S |
San Francisco |
0 |
Only as Proof Set |
5 ct. |
Jefferson - New Obverse |
UNITED STATES |
|
|
- Diameter: 21,25 mm
- Thickness: 1,95 mm
- Weight: 5,00 gr
- 75% Cooper 25% Nickel
|
Cdb |
Year |
Mint |
Mintage |
Notes |
E025007 |
2008D |
Denver |
352.800.000 |
|
5 ct. |
Jefferson - New Obverse |
UNITED STATES |
|
|
- Diameter: 21,25 mm
- Thickness: 1,95 mm
- Weight: 5,00 gr
- 75% Copper 25% Nickel
|
Cdb |
Year |
Mint |
Mintage |
Notes |
E025008 |
2008P |
Philadelphia |
287.760.000 |
|
5 ct. |
Jefferson - New Obverse |
UNITED STATES |
|
|
- Diameter: 21,25 mm
- Thickness: 1,95 mm
- Weight: 5,00 gr
- 75% Cooper 25% Nickel
|
Cdb |
Year |
Mint |
Mintage |
Notes |
E025009 |
2008S |
San Francisco |
0 |
Only as Proof Set |
10 ct. |
Roosevelt |
UNITED STATES |
|
|
- Diameter: 17,90 mm
- Thickness: 1,35 mm
- Weight: 2,27 gr
- 75% Cooper 25% Nickel
|
Cdb |
Year |
Mint |
Mintage |
Notes |
F016141 |
2008D |
Denver |
637.500.000 |
|
10 ct. |
Roosevelt |
UNITED STATES |
|
|
- Diameter: 17,90 mm
- Thickness: 1,35 mm
- Weight: 2,27 gr
- 75% Cooper 25% Nickel
|
Cdb |
Year |
Mint |
Mintage |
Notes |
F016142 |
2008P |
Philadelphia |
413.000.000 |
|
10 ct. |
Roosevelt |
UNITED STATES |
|
|
- Diameter: 17,90 mm
- Thickness: 1,35 mm
- Weight: 2,27 gr
- 75% Cooper 25% Nickel
|
Cdb |
Year |
Mint |
Mintage |
Notes |
F016143 |
2008S |
San Francisco |
0 |
Only as Proof |
F016144 |
2008S |
San Francisco |
0 |
Silver |
25 ct. |
Oklahoma |
UNITED STATES |
|
|
- Diameter: 24,30 mm
- Thickness: 1,75 mm
- Weight: 5,67 gr
- 75% copper and 25% nickel
|
Cdb |
Year |
Mint |
Mintage |
Notes |
G065001 |
2008D |
Denver |
194.600.000 |
|
25 ct. |
Oklahoma |
UNITED STATES |
|
|
- Diameter: 24,30 mm
- Thickness: 1,75 mm
- Weight: 5,67 gr
- 75% copper and 25% nickel
|
Cdb |
Year |
Mint |
Mintage |
Notes |
G065002 |
2008P |
Philadelphia |
222.000.000 |
|
25 ct. |
Oklahoma |
UNITED STATES |
|
|
- Diameter: 24,30 mm
- Thickness: 0,00 mm
- Weight: 5,67 gr
- 75% copper and 25% nickel
|
Cdb |
Year |
Mint |
Mintage |
Notes |
G065003 |
2008S |
San Francisco |
0 |
Only as Proof |
G065004 |
2008S |
San Francisco |
0 |
Silver |
25 ct. |
New Mexico |
UNITED STATES |
|
|
- Diameter: 24,30 mm
- Thickness: 1,75 mm
- Weight: 5,67 gr
- 75% copper and 25% nickel
|
Cdb |
Year |
Mint |
Mintage |
Notes |
G066001 |
2008D |
Denver |
244.400.000 |
|
25 ct. |
New Mexico |
UNITED STATES |
|
|
- Diameter: 24,30 mm
- Thickness: 1,75 mm
- Weight: 5,67 gr
- 75% copper and 25% nickel
|
Cdb |
Year |
Mint |
Mintage |
Notes |
G066002 |
2008P |
Philadelphia |
244.200.000 |
|
25 ct. |
New Mexico |
UNITED STATES |
|
|
- Diameter: 24,30 mm
- Thickness: 1,75 mm
- Weight: 5,67 gr
- 75% copper and 25% nickel
|
Cdb |
Year |
Mint |
Mintage |
Notes |
G066003 |
2008S |
San Francisco |
0 |
Only as Proof |
G066004 |
2008S |
San Francisco |
0 |
Silver |
25 ct. |
Arizona |
UNITED STATES |
|
|
- Diameter: 24,30 mm
- Thickness: 1,75 mm
- Weight: 5,67 gr
- 75% copper and 25% nickel
|
Cdb |
Year |
Mint |
Mintage |
Notes |
G067001 |
2008D |
Denver |
265.000.000 |
|
25 ct. |
Arizona |
UNITED STATES |
|
|
- Diameter: 24,30 mm
- Thickness: 1,75 mm
- Weight: 5,67 gr
- 75% copper and 25% nickel
|
Cdb |
Year |
Mint |
Mintage |
Notes |
G067002 |
2008P |
Philadelphia |
244.600.000 |
|
25 ct. |
Arizona |
UNITED STATES |
|
|
- Diameter: 24,30 mm
- Thickness: 1,75 mm
- Weight: 5,67 gr
- 75% copper and 25% nickel
|
Cdb |
Year |
Mint |
Mintage |
Notes |
G067003 |
2008S |
San Francisco |
0 |
Only as Proof |
G067004 |
2008S |
San Francisco |
0 |
Silver |
25 ct. |
Alaska |
UNITED STATES |
|
|
- Diameter: 24,30 mm
- Thickness: 1,75 mm
- Weight: 5,67 gr
- 75% copper and 25% nickel
|
Cdb |
Year |
Mint |
Mintage |
Notes |
G068001 |
2008D |
Denver |
254.000.000 |
|
25 ct. |
Alaska |
UNITED STATES |
|
|
- Diameter: 24,30 mm
- Thickness: 1,75 mm
- Weight: 5,67 gr
- 75% copper and 25% nickel
|
Cdb |
Year |
Mint |
Mintage |
Notes |
G068002 |
2008P |
Philadelphia |
251.800.000 |
|
25 ct. |
Alaska |
UNITED STATES |
|
|
- Diameter: 24,30 mm
- Thickness: 1,75 mm
- Weight: 5,67 gr
- 75% copper and 25% nickel
|
Cdb |
Year |
Mint |
Mintage |
Notes |
G068003 |
2008S |
San Francisco |
0 |
Only as Proof |
G068004 |
2008S |
San Francisco |
0 |
Silver |
25 ct. |
Hawaii |
UNITED STATES |
|
|
- Diameter: 24,30 mm
- Thickness: 1,75 mm
- Weight: 5,67 gr
- 75% copper and 25% nickel
|
Cdb |
Year |
Mint |
Mintage |
Notes |
G069001 |
2008D |
Denver |
263.600.000 |
|
25 ct. |
Hawaii |
UNITED STATES |
|
|
- Diameter: 24,30 mm
- Thickness: 1,75 mm
- Weight: 5,67 gr
- 75% copper and 25% nickel
|
Cdb |
Year |
Mint |
Mintage |
Notes |
G069002 |
2008P |
Philadelphia |
254.000.000 |
|
25 ct. |
Hawaii |
UNITED STATES |
|
|
- Diameter: 24,30 mm
- Thickness: 1,75 mm
- Weight: 5,67 gr
- 75% copper and 25% nickel
|
Cdb |
Year |
Mint |
Mintage |
Notes |
G069003 |
2008S |
San Francisco |
0 |
Only as Proof |
G069004 |
2008S |
San Francisco |
0 |
Silver |
50 ct. |
Kennedy |
UNITED STATES |
|
|
- Diameter: 30,60 mm
- Thickness: 2,15 mm
- Weight: 11,34 gr
- 75% Cooper 25% Nickel
|
Cdb |
Year |
Mint |
Mintage |
Notes |
H022110 |
2008D |
Denver |
1.700.000 |
|
|
|
|