1 ct. |
Lincoln - Memorial Reverse |
UNITED STATES |
|
|
- Diameter: 19,00 mm
- Thickness: 0,00 mm
- Weight: 2,50 gr
- 97,6% Zinc 2,4% Copper
|
Cdb |
Year |
Mint |
Mintage |
Notes |
B017007 |
1984 |
Philadelphia |
8.151.079.000 |
|
1 ct. |
Lincoln - Memorial Reverse |
UNITED STATES |
|
|
- Diameter: 19,00 mm
- Thickness: 0,00 mm
- Weight: 2,50 gr
- 97,6% Zinc 2,4% Copper
|
Cdb |
Year |
Mint |
Mintage |
Notes |
B017008 |
1984D |
Denver |
5.569.238.906 |
|
1 ct. |
Lincoln - Memorial Reverse |
UNITED STATES |
|
|
- Diameter: 19,00 mm
- Thickness: 0,00 mm
- Weight: 2,50 gr
- 97,6% Zinc 2,4% Copper
|
Cdb |
Year |
Mint |
Mintage |
Notes |
B017009 |
1984S |
San Francisco |
0 |
Only as Proof Set |
5 ct. |
Jefferson |
UNITED STATES |
|
|
- Diameter: 21,20 mm
- Thickness: 0,00 mm
- Weight: 5,00 gr
- 75% Cooper 25% Nickel
|
Cdb |
Year |
Mint |
Mintage |
Notes |
E020095 |
1984D |
Denver |
517.675.146 |
|
5 ct. |
Jefferson |
UNITED STATES |
|
|
- Diameter: 21,20 mm
- Thickness: 0,00 mm
- Weight: 5,00 gr
- 75% Cooper 25% Nickel
|
Cdb |
Year |
Mint |
Mintage |
Notes |
E020096 |
1984P |
Philadelphia |
746.769.000 |
|
5 ct. |
Jefferson |
UNITED STATES |
|
|
- Diameter: 21,20 mm
- Thickness: 0,00 mm
- Weight: 5,00 gr
- 75% Cooper 25% Nickel
|
Cdb |
Year |
Mint |
Mintage |
Notes |
E020097 |
1984S |
San Francisco |
0 |
Only as Proof Set |
10 ct. |
Roosevelt |
UNITED STATES |
|
|
- Diameter: 17,90 mm
- Thickness: 0,00 mm
- Weight: 2,27 gr
- 75% Copper 25% Nickel
|
Cdb |
Year |
Mint |
Mintage |
Notes |
F016052 |
1984D |
Denver |
704.803.976 |
|
10 ct. |
Roosevelt |
UNITED STATES |
|
|
- Diameter: 17,90 mm
- Thickness: 0,00 mm
- Weight: 2,27 gr
- 75% Copper 25% Nickel
|
Cdb |
Year |
Mint |
Mintage |
Notes |
F016053 |
1984P |
Philadelphia |
856.669.000 |
|
10 ct. |
Roosevelt |
UNITED STATES |
|
|
- Diameter: 17,90 mm
- Thickness: 0,00 mm
- Weight: 2,27 gr
- 75% Copper 25% Nickel
|
Cdb |
Year |
Mint |
Mintage |
Notes |
F016054 |
1984S |
San Francisco |
0 |
Only as Proof |
25 ct. |
Washington |
UNITED STATES |
|
|
- Diameter: 24,30 mm
- Thickness: 1,75 mm
- Weight: 5,67 gr
- 75% copper and 25% nickel
|
Cdb |
Year |
Mint |
Mintage |
Notes |
G019022 |
1984D |
Denver |
546.483.064 |
|
25 ct. |
Washington |
UNITED STATES |
|
|
- Diameter: 24,30 mm
- Thickness: 1,75 mm
- Weight: 5,67 gr
- 75% copper and 25% nickel
|
Cdb |
Year |
Mint |
Mintage |
Notes |
G019023 |
1984P |
Philadelphia |
676.545.000 |
|
25 ct. |
Washington |
UNITED STATES |
|
|
- Diameter: 24,30 mm
- Thickness: 1,75 mm
- Weight: 5,67 gr
- 75% copper and 25% nickel
|
Cdb |
Year |
Mint |
Mintage |
Notes |
G019024 |
1984S |
San Francisco |
0 |
Only as Proof |
50 ct. |
Kennedy |
UNITED STATES |
|
|
- Diameter: 30,60 mm
- Thickness: 0,00 mm
- Weight: 11,34 gr
- 75% Copper 25% Nickel
|
Cdb |
Year |
Mint |
Mintage |
Notes |
H022022 |
1984D |
Denver |
26.262.158 |
|
50 ct. |
Kennedy |
UNITED STATES |
|
|
- Diameter: 30,60 mm
- Thickness: 0,00 mm
- Weight: 11,34 gr
- 75% Copper 25% Nickel
|
Cdb |
Year |
Mint |
Mintage |
Notes |
H022023 |
1984P |
Philadelphia |
26.029.000 |
|
50 ct. |
Kennedy |
UNITED STATES |
|
|
- Diameter: 30,60 mm
- Thickness: 0,00 mm
- Weight: 11,34 gr
- 75% Copper 25% Nickel
|
Cdb |
Year |
Mint |
Mintage |
Notes |
H022024 |
1984S |
San Francisco |
0 |
Only as Proof Set |
|
|
|