1 ct. |
Lincoln - Memorial Reverse |
UNITED STATES |
|
|
- Diameter: 19,00 mm
- Thickness: 0,00 mm
- Weight: 2,50 gr
- 97,6% Zinc 2,4% Copper
|
Cdb |
Year |
Mint |
Mintage |
Notes |
B017003 |
1983 |
Philadelphia |
7.752.355.000 |
|
1 ct. |
Lincoln - Memorial Reverse |
UNITED STATES |
|
|
- Diameter: 19,00 mm
- Thickness: 0,00 mm
- Weight: 2,50 gr
- 97,6% Zinc 2,4% Copper
|
Cdb |
Year |
Mint |
Mintage |
Notes |
B017004 |
1983D |
Denver |
6.467.199.428 |
|
1 ct. |
Lincoln - Memorial Reverse |
UNITED STATES |
|
|
- Diameter: 19,00 mm
- Thickness: 0,00 mm
- Weight: 2,50 gr
- 97,6% Zinc 2,4% Copper
|
Cdb |
Year |
Mint |
Mintage |
Notes |
B017005 |
1983S |
San Francisco |
0 |
Only as Proof Set |
5 ct. |
Jefferson |
UNITED STATES |
|
|
- Diameter: 21,20 mm
- Thickness: 0,00 mm
- Weight: 5,00 gr
- 75% Cooper 25% Nickel
|
Cdb |
Year |
Mint |
Mintage |
Notes |
E020092 |
1983D |
Denver |
536.726.276 |
|
5 ct. |
Jefferson |
UNITED STATES |
|
|
- Diameter: 21,20 mm
- Thickness: 0,00 mm
- Weight: 5,00 gr
- 75% Cooper 25% Nickel
|
Cdb |
Year |
Mint |
Mintage |
Notes |
E020093 |
1983P |
Philadelphia |
561.615.000 |
|
5 ct. |
Jefferson |
UNITED STATES |
|
|
- Diameter: 21,20 mm
- Thickness: 0,00 mm
- Weight: 5,00 gr
- 75% Cooper 25% Nickel
|
Cdb |
Year |
Mint |
Mintage |
Notes |
E020094 |
1983S |
San Francisco |
0 |
Only as Proof Set |
10 ct. |
Roosevelt |
UNITED STATES |
|
|
- Diameter: 17,90 mm
- Thickness: 0,00 mm
- Weight: 2,27 gr
- 75% Copper 25% Nickel
|
Cdb |
Year |
Mint |
Mintage |
Notes |
F016049 |
1983D |
Denver |
730.129.224 |
|
10 ct. |
Roosevelt |
UNITED STATES |
|
|
- Diameter: 17,90 mm
- Thickness: 0,00 mm
- Weight: 2,27 gr
- 75% Copper 25% Nickel
|
Cdb |
Year |
Mint |
Mintage |
Notes |
F016050 |
1983P |
Philadelphia |
647.025.000 |
|
10 ct. |
Roosevelt |
UNITED STATES |
|
|
- Diameter: 17,90 mm
- Thickness: 0,00 mm
- Weight: 2,27 gr
- 75% Copper 25% Nickel
|
Cdb |
Year |
Mint |
Mintage |
Notes |
F016051 |
1983S |
San Francisco |
0 |
Only as Proof |
25 ct. |
Washington |
UNITED STATES |
|
|
- Diameter: 24,30 mm
- Thickness: 1,75 mm
- Weight: 5,67 gr
- 75% copper and 25% nickel
|
Cdb |
Year |
Mint |
Mintage |
Notes |
G019019 |
1983D |
Denver |
617.806.446 |
|
25 ct. |
Washington |
UNITED STATES |
|
|
- Diameter: 24,30 mm
- Thickness: 1,75 mm
- Weight: 5,67 gr
- 75% copper and 25% nickel
|
Cdb |
Year |
Mint |
Mintage |
Notes |
G019020 |
1983P |
Philadelphia |
673.535.000 |
|
25 ct. |
Washington |
UNITED STATES |
|
|
- Diameter: 24,30 mm
- Thickness: 1,75 mm
- Weight: 5,67 gr
- 75% copper and 25% nickel
|
Cdb |
Year |
Mint |
Mintage |
Notes |
G019021 |
1983S |
San Francisco |
0 |
Only as Proof |
50 ct. |
Kennedy |
UNITED STATES |
|
|
- Diameter: 30,60 mm
- Thickness: 0,00 mm
- Weight: 11,34 gr
- 75% Copper 25% Nickel
|
Cdb |
Year |
Mint |
Mintage |
Notes |
H022019 |
1983D |
Denver |
32.472.244 |
|
50 ct. |
Kennedy |
UNITED STATES |
|
|
- Diameter: 30,60 mm
- Thickness: 0,00 mm
- Weight: 11,34 gr
- 75% Copper 25% Nickel
|
Cdb |
Year |
Mint |
Mintage |
Notes |
H022020 |
1983P |
Philadelphia |
34.139.000 |
|
50 ct. |
Kennedy |
UNITED STATES |
|
|
- Diameter: 30,60 mm
- Thickness: 0,00 mm
- Weight: 11,34 gr
- 75% Copper 25% Nickel
|
Cdb |
Year |
Mint |
Mintage |
Notes |
H022021 |
1983S |
San Francisco |
0 |
Only as Proof Set |
|
|
|