1 ct. |
Lincoln |
UNITED STATES |
|
|
- Diameter: 19,00 mm
- Thickness: 0,00 mm
- Weight: 3,11 gr
- 95% Cooper 5% Tin and Zinc
|
Cdb |
Year |
Mint |
Mintage |
Notes |
B013086 |
1940 |
Philadelphia |
586.825.872 |
|
1 ct. |
Lincoln |
UNITED STATES |
|
|
- Diameter: 19,00 mm
- Thickness: 0,00 mm
- Weight: 3,11 gr
- 95% Cooper 5% Tin and Zinc
|
Cdb |
Year |
Mint |
Mintage |
Notes |
B013087 |
1940D |
Denver |
81.390.000 |
|
1 ct. |
Lincoln |
UNITED STATES |
|
|
- Diameter: 19,00 mm
- Thickness: 0,00 mm
- Weight: 3,11 gr
- 95% Cooper 5% Tin and Zinc
|
Cdb |
Year |
Mint |
Mintage |
Notes |
B013088 |
1940S |
San Francisco |
112.940.000 |
|
5 ct. |
Jefferson |
UNITED STATES |
|
|
- Diameter: 21,20 mm
- Thickness: 0,00 mm
- Weight: 5,00 gr
- 75% Cooper 25% Nickel
|
Cdb |
Year |
Mint |
Mintage |
Notes |
E018007 |
1940 |
Philadelphia |
176.485.000 |
|
5 ct. |
Jefferson |
UNITED STATES |
|
|
- Diameter: 21,20 mm
- Thickness: 0,00 mm
- Weight: 5,00 gr
- 75% Cooper 25% Nickel
|
Cdb |
Year |
Mint |
Mintage |
Notes |
E018008 |
1940D |
Denver |
43.540.000 |
|
5 ct. |
Jefferson |
UNITED STATES |
|
|
- Diameter: 21,20 mm
- Thickness: 0,00 mm
- Weight: 5,00 gr
- 75% Cooper 25% Nickel
|
Cdb |
Year |
Mint |
Mintage |
Notes |
E018009 |
1940S |
San Francisco |
39.690.000 |
|
10 ct. |
Mercury |
UNITED STATES |
|
|
- Diameter: 17,90 mm
- Thickness: 0,00 mm
- Weight: 2,50 gr
- 90% Silver 10% Copper
|
Cdb |
Year |
Mint |
Mintage |
Notes |
F014060 |
1940 |
Philadelphia |
65.350.000 |
|
10 ct. |
Mercury |
UNITED STATES |
|
|
- Diameter: 17,90 mm
- Thickness: 0,00 mm
- Weight: 2,50 gr
- 90% Silver 10% Copper
|
Cdb |
Year |
Mint |
Mintage |
Notes |
F014061 |
1940D |
Denver |
21.198.000 |
|
10 ct. |
Mercury |
UNITED STATES |
|
|
- Diameter: 17,90 mm
- Thickness: 0,00 mm
- Weight: 2,50 gr
- 90% Silver 10% Copper
|
Cdb |
Year |
Mint |
Mintage |
Notes |
F014062 |
1940S |
San Francisco |
21.560.000 |
|
25 ct. |
Washington |
UNITED STATES |
|
|
- Diameter: 24,30 mm
- Thickness: 0,00 mm
- Weight: 6,25 gr
- 90% Silver 10% Copper
|
Cdb |
Year |
Mint |
Mintage |
Notes |
G016020 |
1940 |
Philadelphia |
35.704.000 |
|
25 ct. |
Washington |
UNITED STATES |
|
|
- Diameter: 24,30 mm
- Thickness: 0,00 mm
- Weight: 6,25 gr
- 90% Silver 10% Copper
|
Cdb |
Year |
Mint |
Mintage |
Notes |
G016021 |
1940D |
Denver |
2.797.600 |
|
25 ct. |
Washington |
UNITED STATES |
|
|
- Diameter: 24,30 mm
- Thickness: 0,00 mm
- Weight: 6,25 gr
- 90% Silver 10% Copper
|
Cdb |
Year |
Mint |
Mintage |
Notes |
G016022 |
1940S |
San Francisco |
8.244.000 |
|
50 ct. |
Walking Liberty - Mintmark on reverse |
UNITED STATES |
|
|
- Diameter: 30,60 mm
- Thickness: 0,00 mm
- Weight: 12,50 gr
- 90% Silver 10% Copper
|
Cdb |
Year |
Mint |
Mintage |
Notes |
H016039 |
1940 |
Philadelphia |
9.156.000 |
|
50 ct. |
Walking Liberty - Mintmark on reverse |
UNITED STATES |
|
|
- Diameter: 30,60 mm
- Thickness: 0,00 mm
- Weight: 12,50 gr
- 90% Silver 10% Copper
|
Cdb |
Year |
Mint |
Mintage |
Notes |
H016040 |
1940S |
San Francisco |
4.550.000 |
|
|
|
|