1 ct. |
Lincoln |
UNITED STATES |
|
|
- Diameter: 19,00 mm
- Thickness: 0,00 mm
- Weight: 3,11 gr
- 95% Cooper 5% Tin and Zinc
|
Cdb |
Year |
Mint |
Mintage |
Notes |
B013080 |
1938 |
Philadelphia |
156.696.734 |
|
1 ct. |
Lincoln |
UNITED STATES |
|
|
- Diameter: 19,00 mm
- Thickness: 0,00 mm
- Weight: 3,11 gr
- 95% Cooper 5% Tin and Zinc
|
Cdb |
Year |
Mint |
Mintage |
Notes |
B013081 |
1938D |
Denver |
20.010.000 |
|
1 ct. |
Lincoln |
UNITED STATES |
|
|
- Diameter: 19,00 mm
- Thickness: 0,00 mm
- Weight: 3,11 gr
- 95% Cooper 5% Tin and Zinc
|
Cdb |
Year |
Mint |
Mintage |
Notes |
B013082 |
1938S |
San Francisco |
15.180.000 |
|
5 ct. |
Buffalo - Line Type |
UNITED STATES |
|
|
- Diameter: 21,20 mm
- Thickness: 0,00 mm
- Weight: 5,00 gr
- 75% Cooper 25% Nickel
|
Cdb |
Year |
Mint |
Mintage |
Notes |
E017061 |
1938D |
Denver |
7.020.000 |
|
5 ct. |
Jefferson |
UNITED STATES |
|
|
- Diameter: 21,20 mm
- Thickness: 0,00 mm
- Weight: 5,00 gr
- 75% Cooper 25% Nickel
|
Cdb |
Year |
Mint |
Mintage |
Notes |
E018001 |
1938 |
Philadelphia |
19.496.000 |
|
5 ct. |
Jefferson |
UNITED STATES |
|
|
- Diameter: 21,20 mm
- Thickness: 0,00 mm
- Weight: 5,00 gr
- 75% Cooper 25% Nickel
|
Cdb |
Year |
Mint |
Mintage |
Notes |
E018002 |
1938D |
Denver |
5.376.000 |
|
5 ct. |
Jefferson |
UNITED STATES |
|
|
- Diameter: 21,20 mm
- Thickness: 0,00 mm
- Weight: 5,00 gr
- 75% Cooper 25% Nickel
|
Cdb |
Year |
Mint |
Mintage |
Notes |
E018003 |
1938S |
San Francisco |
4.105.000 |
|
10 ct. |
Mercury |
UNITED STATES |
|
|
- Diameter: 17,90 mm
- Thickness: 0,00 mm
- Weight: 2,50 gr
- 90% Silver 10% Copper
|
Cdb |
Year |
Mint |
Mintage |
Notes |
F014054 |
1938 |
Philadelphia |
22.190.000 |
|
10 ct. |
Mercury |
UNITED STATES |
|
|
- Diameter: 17,90 mm
- Thickness: 0,00 mm
- Weight: 2,50 gr
- 90% Silver 10% Copper
|
Cdb |
Year |
Mint |
Mintage |
Notes |
F014055 |
1938D |
Denver |
5.537.000 |
|
10 ct. |
Mercury |
UNITED STATES |
|
|
- Diameter: 17,90 mm
- Thickness: 0,00 mm
- Weight: 2,50 gr
- 90% Silver 10% Copper
|
Cdb |
Year |
Mint |
Mintage |
Notes |
F014056 |
1938S |
San Francisco |
8.090.000 |
|
25 ct. |
Washington |
UNITED STATES |
|
|
- Diameter: 24,30 mm
- Thickness: 0,00 mm
- Weight: 6,25 gr
- 90% Silver 10% Copper
|
Cdb |
Year |
Mint |
Mintage |
Notes |
G016015 |
1938 |
Philadelphia |
9.480.000 |
|
25 ct. |
Washington |
UNITED STATES |
|
|
- Diameter: 24,30 mm
- Thickness: 0,00 mm
- Weight: 6,25 gr
- 90% Silver 10% Copper
|
Cdb |
Year |
Mint |
Mintage |
Notes |
G016016 |
1938S |
San Francisco |
2.832.000 |
|
50 ct. |
Walking Liberty - Mintmark on reverse |
UNITED STATES |
|
|
- Diameter: 30,60 mm
- Thickness: 0,00 mm
- Weight: 12,50 gr
- 90% Silver 10% Copper
|
Cdb |
Year |
Mint |
Mintage |
Notes |
H016034 |
1938 |
Philadelphia |
4.110.000 |
|
50 ct. |
Walking Liberty - Mintmark on reverse |
UNITED STATES |
|
|
- Diameter: 30,60 mm
- Thickness: 0,00 mm
- Weight: 12,50 gr
- 90% Silver 10% Copper
|
Cdb |
Year |
Mint |
Mintage |
Notes |
H016035 |
1938D |
Denver |
491.600 |
|
|
|
|