1 ct. |
Lincoln |
UNITED STATES |
|
|
- Diameter: 19,00 mm
- Thickness: 0,00 mm
- Weight: 3,11 gr
- 95% Cooper 5% Tin and Zinc
|
Cdb |
Year |
Mint |
Mintage |
Notes |
B013026 |
1918 |
Philadelphia |
288.104.634 |
|
1 ct. |
Lincoln |
UNITED STATES |
|
|
- Diameter: 19,00 mm
- Thickness: 0,00 mm
- Weight: 3,11 gr
- 95% Cooper 5% Tin and Zinc
|
Cdb |
Year |
Mint |
Mintage |
Notes |
B013027 |
1918D |
Denver |
47.830.000 |
|
1 ct. |
Lincoln |
UNITED STATES |
|
|
- Diameter: 19,00 mm
- Thickness: 0,00 mm
- Weight: 3,11 gr
- 95% Cooper 5% Tin and Zinc
|
Cdb |
Year |
Mint |
Mintage |
Notes |
B013028 |
1918S |
San Francisco |
34.680.000 |
|
5 ct. |
Buffalo - Line Type |
UNITED STATES |
|
|
- Diameter: 21,20 mm
- Thickness: 0,00 mm
- Weight: 5,00 gr
- 75% Cooper 25% Nickel
|
Cdb |
Year |
Mint |
Mintage |
Notes |
E017016 |
1918 |
Philadelphia |
32.086.314 |
|
5 ct. |
Buffalo - Line Type |
UNITED STATES |
|
|
- Diameter: 21,20 mm
- Thickness: 0,00 mm
- Weight: 5,00 gr
- 75% Cooper 25% Nickel
|
Cdb |
Year |
Mint |
Mintage |
Notes |
E017017 |
1918D |
Denver |
8.362.000 |
|
5 ct. |
Buffalo - Line Type |
UNITED STATES |
|
|
- Diameter: 21,20 mm
- Thickness: 0,00 mm
- Weight: 5,00 gr
- 75% Cooper 25% Nickel
|
Cdb |
Year |
Mint |
Mintage |
Notes |
E017018 |
1918S |
San Francisco |
4.882.000 |
|
10 ct. |
Mercury |
UNITED STATES |
|
|
- Diameter: 17,90 mm
- Thickness: 0,00 mm
- Weight: 2,50 gr
- 90% Silver 10% Copper
|
Cdb |
Year |
Mint |
Mintage |
Notes |
F014007 |
1918 |
Philadelphia |
26.680.000 |
|
10 ct. |
Mercury |
UNITED STATES |
|
|
- Diameter: 17,90 mm
- Thickness: 0,00 mm
- Weight: 2,50 gr
- 90% Silver 10% Copper
|
Cdb |
Year |
Mint |
Mintage |
Notes |
F014008 |
1918D |
Denver |
19.300.000 |
|
10 ct. |
Mercury |
UNITED STATES |
|
|
- Diameter: 17,90 mm
- Thickness: 0,00 mm
- Weight: 2,50 gr
- 90% Silver 10% Copper
|
Cdb |
Year |
Mint |
Mintage |
Notes |
F014009 |
1918S |
San Francisco |
22.674.800 |
|
25 ct. |
Standing Liberty - Type II |
UNITED STATES |
|
|
- Diameter: 24,30 mm
- Thickness: 0,00 mm
- Weight: 6,25 gr
- 90% Silver 10% Copper
|
Cdb |
Year |
Mint |
Mintage |
Notes |
G015004 |
1918 |
Philadelphia |
14.240.000 |
|
25 ct. |
Standing Liberty - Type II |
UNITED STATES |
|
|
- Diameter: 24,30 mm
- Thickness: 0,00 mm
- Weight: 6,25 gr
- 90% Silver 10% Copper
|
Cdb |
Year |
Mint |
Mintage |
Notes |
G015005 |
1918D |
Denver |
7.380.000 |
|
25 ct. |
Standing Liberty - Type II |
UNITED STATES |
|
|
- Diameter: 24,30 mm
- Thickness: 0,00 mm
- Weight: 6,25 gr
- 90% Silver 10% Copper
|
Cdb |
Year |
Mint |
Mintage |
Notes |
G015006 |
1918S |
San Francisco |
11.072.000 |
|
50 ct. |
Walking Liberty - Mintmark on reverse |
UNITED STATES |
|
|
- Diameter: 30,60 mm
- Thickness: 0,00 mm
- Weight: 12,50 gr
- 90% Silver 10% Copper
|
Cdb |
Year |
Mint |
Mintage |
Notes |
H016004 |
1918 |
Philadelphia |
6.634.000 |
|
50 ct. |
Walking Liberty - Mintmark on reverse |
UNITED STATES |
|
|
- Diameter: 30,60 mm
- Thickness: 0,00 mm
- Weight: 12,50 gr
- 90% Silver 10% Copper
|
Cdb |
Year |
Mint |
Mintage |
Notes |
H016005 |
1918D |
Denver |
3.853.040 |
|
50 ct. |
Walking Liberty - Mintmark on reverse |
UNITED STATES |
|
|
- Diameter: 30,60 mm
- Thickness: 0,00 mm
- Weight: 12,50 gr
- 90% Silver 10% Copper
|
Cdb |
Year |
Mint |
Mintage |
Notes |
H016006 |
1918S |
San Francisco |
10.282.000 |
|
|
|
|